Scope of this guide
This management guide translates the process into cost, risk and throughput: what to measure, what to audit and where the money leaks.
Process: Resin Dripping. Figures in this guide are industry-standard starting ranges; confirm against your supplier TDS before locking settings.
Working ranges and control points
The table below is the daily reference for a dripping station. Set by the card, verify by the control point column.
| Parameter | Typical range | Control point | Watch out |
|---|---|---|---|
| Mix ratio | By resin kit (A:B) | Scale 0.1 g accuracy | Off-ratio never cures fully |
| Degassing | Vacuum 2–5 min after mix | No visible bubbles | Skipped step craters |
| Pot life | 20–60 min by kit | Discard at pot end | Thickened resin traps bubbles |
| Cure | 40–60 °C × 60–120 min | Profile per thickness | Thick pour exotherms |
| Bubble count QC | 0 visible > 0.3 mm | Light table per batch | Cold resin is viscous |
Run It As A Business: the management view
Beyond the basic card, this is the layer that matters at your level:
| Cost line | What drives it | Metric to track | Typical lever |
|---|---|---|---|
| Chemicals | Drag-out and bath dumps | Cost per 1000 parts | Rinse counter-flow, drip bars |
| Rework | First-pass yield losses | FPY by defect family | Fix top family first |
| Energy | Heated tanks and idle time | kWh per 1000 parts | Covers, night setback |
| Claims | Escape rate | PPM by customer | Ship gate on FPY |
Standard routine
- Warm resin to 25–30 °C for flow
- Scale A and B exactly; stir slowly 2–3 min
- Degas before pouring, not after
- Pour centre-out to let self-level
- Cure with profile, log oven load
Engineer notes
- Stir fast and you whip bubbles in — slow folding wins
- Pot life shortens in summer; batch smaller
- Thick pours need stepped cure to avoid exotherm yellowing
- Dust-free covers over racks during gel
- Yellowing traces to over-heat or aged hardener
Safety: Uncured resin and hardener are skin sensitisers. Nitrile gloves, no latex, and barrier cream; ventilate the curing oven.
FAQ
Why do bubbles keep appearing after degassing?
Cold resin or over-fast stirring. Warm components and fold slowly; degas again if needed.
Can I speed cure with more hardener?
No — off-ratio leaves uncured resin. Follow kit ratio and raise temperature instead.
Why does the surface stay tacky?
Off-ratio mix or expired pot life. Scale exactly and mix fresh within pot life.
Which single metric should I start reporting weekly?
First-pass yield by defect family; it exposes rework cost and points at the largest lever.